Conductive thin coating made of AgNWs
From Hackteria Wiki
Preparation of AgNWs solutions
The wet slurry AgNWs in diameter <100nm, length >30nm purchased from Taobao supplier was mixed in IPA solution to a concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent.
Material lists
- Polyvinyl butyral (PVB) powders 100g
- DMF 1L
- hexamethylene diisocyanate (HDI) 15g
- Isopropyl alcohol (IPA) 1L
- AgNWs 1g
References
- Dong Jun Lee1, Youngsu Oh, Jae-Min Hong, Young Wook Park & Byeong-Kwon Ju. (2018). Light sintering of ultra-smooth and robust silver nanowire networks embedded in poly(vinyl-butyral) for flexible OLED.
- Fang-Cheng Liang, You-Wei Chang, Chi-Ching Kuo, Chia-Jung Cho, Dai-Hua Jiang, Fu-Cheng Jhuang, Syang-Peng Rweia, and Redouane Borsali. (2018). A Mechanically Robust Silver Nanowire–Polydimethylsiloxane Electrode Based on Facile Transfer Printing Techniques for Wearable Displays.
- What is the best way to disperse AgNW in solution, for spin-coating on PDMS substrate? https://www.researchgate.net/post/What-is-the-best-way-to-disperse-AgNW-in-solution-for-spin-coating-on-PDMS-substrate