==Preparation of AgNWs solutions==
 
==Preparation of AgNWs solutions==
−
The wet slurry AgNWs in diameter <100nm, length >30nm purchased from [https://item.taobao.com/item.htm?spm=a1z09.2.0.0.72f92e8dvw2Bxy&id=633022810999&_u=22f32sdpd457 Taobao supplier] was mixed in IPA solution to a concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent.
+
The wet slurry AgNWs in diameter <100nm, length >30nm purchased from [https://item.taobao.com/item.htm?spm=a1z09.2.0.0.72f92e8dvw2Bxy&id=633022810999&_u=22f32sdpd457 Taobao supplier] was mixed in Isopropyl alcohol (IPA) solution at concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent.
  
 
==Material lists==
 
==Material lists==

Revision as of 15:38, 2 October 2023

Preparation of AgNWs solutions

The wet slurry AgNWs in diameter <100nm, length >30nm purchased from Taobao supplier was mixed in Isopropyl alcohol (IPA) solution at concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent.

Material lists

  1. Polyvinyl butyral (PVB) powders 100g
  2. Dimethylformamide (DMF) 1L
  3. Hexamethylene diisocyanate (HDI) 15g
  4. Isopropyl alcohol (IPA) 1L
  5. AgNWs 1g

References

  1. Dong Jun Lee1, Youngsu Oh, Jae-Min Hong, Young Wook Park & Byeong-Kwon Ju. (2018). Light sintering of ultra-smooth and robust silver nanowire networks embedded in poly(vinyl-butyral) for flexible OLED.
  2. Fang-Cheng Liang, You-Wei Chang, Chi-Ching Kuo, Chia-Jung Cho, Dai-Hua Jiang, Fu-Cheng Jhuang, Syang-Peng Rweia, and Redouane Borsali. (2018). A Mechanically Robust Silver Nanowire–Polydimethylsiloxane Electrode Based on Facile Transfer Printing Techniques for Wearable Displays.
  3. What is the best way to disperse AgNW in solution, for spin-coating on PDMS substrate? https://www.researchgate.net/post/What-is-the-best-way-to-disperse-AgNW-in-solution-for-spin-coating-on-PDMS-substrate
Retrieved from "http://www.hackteria.org/wiki/index.php?title=Conductive_thin_coating_made_of_AgNWs&oldid=54049"